Efficacy of an experimental gaseous ozone-based sterilization method for clear aligners.

OBJECTIVES: To assess effectiveness of an experimental sterilization method based on the exposure of an O3/O2 gas mixture directly inside the packaging for clear aligners. MATERIALS AND METHODS: Fifty samples consisting of pieces of polyethylene terephthalate glycol (PET-G) aligners were contaminated by manual handling and subsequently divided into different groups (n = 30 for exposure to O3/O2 gas at different times, n = 10 for positive control with 2% chlorhexidine digluconate, n = 10 for negative control). The measurement of optical densities (OD) of the initial and final microbial cultures was recorded for all groups. Kruskal-Wallis test was used for differences between groups while Wilcoxon test was used to compare initial and final OD values within groups. Statistical significance was set at P < .05. RESULTS: Comparison within the groups showed statistically significant differences for exposure to the gaseous mixture (72 hours), for positive and negative controls. Other significant differences were found in the multiple comparisons between the application of gaseous ozone (48 hours and 72 hours) and the negative control. CONCLUSIONS: The direct exposure of gaseous ozone on the aligners inside their packaging showed microbicidal capacity at 72 hours, which was equivalent to the positive control with immersion in chlorhexidine digluconate. This innovative sterilization procedure could be considered in the final manufacturing processes of clear aligners to eliminate the potentially pathogenic microorganisms that are deposited on surfaces of these orthodontic devices.

Chemical-Physical Characterization of PET-G-Based Material for Orthodontic Use: Preliminary Evaluation of micro-Raman Analysis.

OBJECTIVES: Orthodontic treatment with clear thermoplastic aligners is in great demand by patients especially for aesthetics. Any alterations in the chemical composition of the thermoplastic material for aligners, subjected to the oral environment and exposure to various commonly used substances, could influence the desired orthodontic movement decreasing the predictability of the treatment. The objective of this study was to determine the chemical-physical characterization by micro-Raman spectroscopy of a thermoplastic material based on polyethylene terephthalate glycol (PET-G) used for the manufacture of Lineo aligners (Micerium Lab, Avegno, Italy) subjected to different staining beverages and cleaning agents. MATERIALS AND METHODS: Twenty-two thermoformed PET-G samples were immersed to various substances of daily use for 10 and 15 days (coffee, tea, Coca-Cola, red wine, colloidal silver disinfectant, nicotine, artificial saliva, cigarette smoke, and different combinations of saliva with some of the previous solutions). Subsequently, the chemical-physical characterization was investigated by micro-Raman spectroscopy. RESULTS: The analysis of the spectra acquired for all the specimens showed no difference in the exposure to the different solvents at 10 and 15 days. Furthermore, having ascertained the heterogeneous surface morphology of the PET-G material due to thermoforming, various deposits were present on all the samples whose consistency and concentration depended on the substance used. CONCLUSION: The spectroscopic investigations have provided a precise and detailed analysis of the qualitative and structural data of the PET-G material under examination. No significant structural modifications of the thermoplastic polymer were found after immersion in different solutions in the exposure times adopted.